You can eliminate any "porosity" in alcohol-epoxy mixture by not using too much alcohol and leaving it to cure in a cooler place in the house to avoid rapid outgassing that may lead to the "porosity".

Even if there's any "porosity" it's normally "closed porosity" and not "open porosity". Fuel should not seep through that layer as per Minnflyer. Did I cause enough confusion ?