I MOSTLY use titebond glue. C A is too smelly and you can't go arround with you fingers stuck together
all the time. you cant get it off your fingers either. Epoxy is great, because it fills gaps , and it washes off your hands with lac thinner or acetone. Tite bond is the way to go , because it is water based, AND SANDS SOMEWHAT. C A WILL NOT SAND. EPOXY also is tough to sand. In critical areas AND areas that need to be fuel proof i ALWAYS use Epoxy.


have a goody


Dan